BP 2014 is a white epoxy laminating resin which provides quick wet-out of fiberglass cloth with easy brushing characteristics, while keeping run-off from vertical surfaces to a minimum. The resin is color indicated (green) and will turn white as the hardener is mixed into the resin. This indicator system promotes fast and efficient mixing of the resin and hardener, insuring that they are thoroughly mixed yet wasting no time overmixing. Fiberglass laminates made with BP 2014 will have excellent physical properties when used for structural parts.

Features:
Mix ratio(by wt.): 100:20
Viscosity (mixed): 2,700cps
Pot life (min): 35
Cure time (hrs)(72°F): 16
Tensile strength(psi): 31,500
Flexural strength (psi): 38,100
Compressive strength(psi): 27,600
Heat Deflection (°F): 160
Color: White
Datasheet

BP 2019 is a clear-amber epoxy laminating/adhesive resin formulated especially for the bonding of wood and urethane model board. The resin is color indicated (green) and will turn to a clear amber color as the hardener is mixed into the resin. This indicator system promotes fast and efficient mixing of the resin and hardener, insuring that they are thoroughly mixed yet wasting no time overmixing. BP2019 can also be used aas a quick set laminating resin for those needing quick bonding to exisiting laminate. The BP2019's 30 minute pot-life and bond strength allows for added repair strength and wetting to allow for quick marine and automotive applications.

Features:
Mix ratio(by wt.): 100:25
Viscosity (mixed): 2,100cps
Pot life (min): 30
Cure time (hrs)(72°F): 16
Hardness (shore): 80D
Heat Deflection (°F):160
Color: Gray
Datasheet

BP 2022 is a white epoxy laminating resin which provides a laminate of exceptional dimensional stability. The resin is color indicated (green) and will turn white as the hardener is mixed into the resin. This indicator system promotes fast and efficient mixing of the resin and hardener, insuring that they are thoroughly mixed yet wasting no time overmixing. BP 2022 provides quick wet-out of fiberglass cloth with easy brushing characteristics, while keeping run-off from vertical surfaces to a minimum.

Features:
Mix ratio(by wt.): 100:20
Viscosity (mixed): 1,900cps
Pot life (min): 35
Cure time (hrs)(72°F): 16
Tensile strength(psi): 52,500
Flexural strength (psi): N/A
Compressive strength(psi): 41,500
Hardness(shore): 85D
Color: White
Datasheet

BP 2186 is a high-temperature, aluminum-filled epoxy laminating resin which provides easy brushing characteristics and quick wet-out of fiberglass cloth, while at the same time limiting run-off from vertical surfaces to a minimum. BP 2186 is formulated to have minimum skin irritation potential and avoids all carcinogenic materials in both the resin and hardener.

Features:
Mix ratio(by wt.): 100:14
Viscosity (mixed): 4,100cps
Pot life (min): 55
*Cure time (hrs)(72°F): 16
Heat Deflection(°F): 240
Hardness(shore): 85D
Color: Gray
Datasheet
*note: different cure schedule in the case of high temp tools

BP 2191 is a high-temperature, aluminum-filled epoxy laminating resin which provides easy brushing characteristics and quick wet-out of fiberglass cloth, while at the same time limiting run-off from vertical surfaces to a minimum. BP 2191 is formulated to have minimum skin irritation potential and avoids all carcinogenic materials in both the resin and hardener.

Features:
Mix ratio(by wt.): 100:15
Viscosity (mixed): 4,100cps
Pot life (min): 140
*Cure time (hrs)(72°F): See Datasheet
Heat Deflection(°F): 315
Hardness(shore): 85D
Color: Gray
Datasheet
*note: different cure schedule in the case of high temp tools